the surface of nanoparticle silicon as studied by solid-state nmr
Clicks: 187
ID: 186088
2012
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
187 views
37 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #384 of 461 articles by views in Nature Materials
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 461 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The surface structure and adjacent interior of commercially available silicon nanopowder (np-Si) was studied using multinuclear, solid-state NMR spectroscopy. The results are consistent with an overall picture in which the bulk of the np-Si interior consists of highly ordered (“crystalline”) silicon atoms, each bound tetrahedrally to four other silicon atoms. From a combination of 1H, 29Si and 2H magic-angle-spinning (MAS) NMR results and quantum mechanical 29Si chemical shift calculations, silicon atoms on the surface of “as-received” np-Si were found to exist in a variety of chemical structures, with apparent populations in the order (a) (Si–O–)3Si–H > (b) (Si–O–)3SiOH > (c) (HO–)nSi(Si)m(–OSi)4−m−n ≈ (d) (Si–O–)2Si(H)OH > (e) (Si–O–)2Si(–OH)2 > (f) (Si–O–)4Si, where Si stands for a surface silicon atom and Si represents another silicon atom that is attached to Si by either a Si–Si bond or a Si–O–Si linkage. The relative populations of each of these structures can be modified by chemical treatment, including with O2 gas at elevated temperature. A deliberately oxidized sample displays an increased population of (Si–O–)3Si–H, as well as (Si–O–)3SiOH sites. Considerable heterogeneity of some surface structures was observed. A combination of 1H and 2H MAS experiments provide evidence for a substantial population of silanol (Si–OH) moieties, some of which are not readily H-exchangeable, along with the dominant Si–H sites, on the surface of “as-received” np-Si; the silanol moieties are enhanced by deliberate oxidation. An extension of the DEPTH background suppression method is also demonstrated that permits measurement of the T2 relaxation parameter simultaneously with background suppression.
| Reference Key |
maciel2012materialsthe
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Gary E. Maciel;Takeshi Kobayashi;Joseph A. DiVerdi;Yuan Yang;Rebecca A. Faulkner |
| Journal | Nature Materials |
| Year | 2012 |
| DOI |
10.3390/ma6010018
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.