combustion synthesis and photoluminescence properties of red-emitting caalsin3:eu2+ phosphor for white-leds
Clicks: 183
ID: 154122
2014
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
183 views
17 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #390 of 461 articles by views in Nature Materials
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 461 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
A combustion synthesis method has been developed for synthesis of Eu2+ doped CaAlSiN3 phosphor and its photoluminescence properties were investigated. Ca, Al, Si, and Eu2O3 powders were used as the Ca, Al, Si and Eu sources. The addition of NaN3, NH4Cl and Si3N4 powders was found to increase significantly the product yield. These powders were mixed and pressed into a compact, which was then wrapped up with an igniting agent (i.e., Mg+Fe3O4). The compact was ignited by electrical heating under a N2 pressure of ≤1.0 MPa. Effects of these experimental parameters on the product yield were investigated and a reaction mechanism was proposed. The synthesized CaAlSiN3:Eu2+ phosphor absorbs light in the region of 200–600 nm and shows a broad band emission in the region of 500–800 nm due to the 4f65d1 → 4f7 transition of Eu2+. The sample doped with Eu2+ at the optimized molar ratio of 0.04 is efficiently excited by the blue light (460 nm) and generates emission peaking at ~650 nm with peak emission intensity ~106% of a commercially available phosphor, YAG:Ce3+(P46-Y3).The internal quantum efficiency of the synthesized phosphor was measured to be 71%, compared to 69% of the YAG:Ce3+ (P46-Y3).
| Reference Key |
chung2014materialscombustion
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Shyan-Lung Chung;Shu-Chi Huang |
| Journal | Nature Materials |
| Year | 2014 |
| DOI |
10.3390/ma7127828
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.