Slag recycling in submerged arc welding and its effects on the quality of stainless steel claddings
Clicks: 452
ID: 71037
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
83.2
/100
452 views
313 readers
Trending
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #8 of 88 articles by views in materials & design
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
A novel technology for recycling of slag waste generated during submerged arc cladding of stainless steel (SS) was developed. The claddings produced using “recycled slag” were analysed for their quality and performance during service. The chemical composition of these claddings was found to be within the acceptable range of American Society of Mechanical Engineers (ASME) specifications. Their resistance to various types of corrosion, as determined by conducting different standard emersion and electrochemical tests, was found to be at par with the claddings produced with fresh flux. Results of bend test indicate that these claddings possess good mechanical properties and bond integrity with the substrate at all points. The microstructure examination revealed that both types of claddings (deposited with fresh flux and recycled slag) solidified in same mode of solidification and have similar grain size, shape and phase distribution, in all zones. The microhardness values of the deposited metal, heat affected zone and base metal for both types of cladding are comparable. Ferrite measurements done theoretically as well as practically showed the presence of adequate amount of ferrite to prevent hot fissuring. The cost of recycled slag was calculated and found to be 73% less than the equivalent fresh flux. Keywords: Weld cladding, Submerged arc welding (SAW), Slag recycling, Stainless steel, Corrosion testing
| Reference Key |
garg2016slagmaterials
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Garg, Jatinder;Singh, Kulwant; |
| Journal | materials & design |
| Year | 2016 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.