microscopic investigations of axial zones of continuous casting ingots
Clicks: 168
ID: 244574
2015
Article Quality & Performance Metrics
Overall Quality
Improving Quality
0.0
/100
Combines engagement data with AI-assessed academic quality
Reader Engagement
Emerging Content
5.7
/100
19 views
19 readers
Trending
AI Quality Assessment
Not analyzed
Abstract
This paper presents the results of microscopic investigations of the structure and chemical composition of the axial zones of continuous casting ingots of 140 x 140 mm cross-section made of G3Si1 steel, comprising the areas of porosityand axial shrinkage defects. The occurrence of shrinkage hollows and non-metallic phase, resulting from chemical reactions of the steel components with oxygen at the solidification front, has been stated in these areas.
| Reference Key |
janiszewski2015metalurgijamicroscopic
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;K. Janiszewski |
| Journal | journal of the formosan medical association = taiwan yi zhi |
| Year | 2015 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.