formation and dissolution of γ’ precipitates in in792 superalloy at elevated temperatures
Clicks: 257
ID: 243452
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
257 views
30 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #51 of 136 articles by views in seminars in cancer biology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 136 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Precipitation of γ’ phase in nickel-base superalloy IN792-5A was studied using in-situ Small Angle Neutron Scattering (SANS). It was found that additional precipitates are formed after reheating above 600 °C when the material is previously fast cooled (100 K/min) from 900 °C. The size distribution and volume fraction of the additional γ’ precipitates as well as of the already present medium-size precipitates in dependence on temperature were evaluated. The small precipitates can influence mechanical properties of the alloy, which exhibits an anomaly in the temperature dependence of the yield stress. Volume fraction of all precipitate populations above 900 °C was estimated as well.
| Reference Key |
strunz2016metalsformation
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Pavel Strunz;Martin Petrenec;Jaroslav Polák;Urs Gasser;Gergely Farkas |
| Journal | seminars in cancer biology |
| Year | 2016 |
| DOI |
10.3390/met6020037
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.