effect of al substitution on structural, magnetic, and magnetocaloric properties of er6fe23−xalx (x = 0 and 3) intermetallic compounds
Clicks: 239
ID: 230283
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
239 views
52 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #46 of 88 articles by views in turk kardiyoloji dernegi arsivi
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The structural, magnetic, and magnetocaloric properties of Er6Fe23−xAlx (x = 0 and 3) intermetallic compounds have been studied systematically. Samples were prepared using the arc furnace by annealing at 1073 K for one week. Rietveld analysis of XRD shows the formation of pure crystalline phase with cubic Fm-3m structure. Refinement results show that the unit cell volume decreases with increasing Al content. The Curie temperature Tc of the prepared samples was found to be strongly dependent on the aluminum content. This reduces magnetization and the ferrimagnetic phase transition temperature (Tc) from 481 K (for x = 0) to 380 K (for x = 3), is due to the substitution of magnetic element (Fe) by non-magnetic atoms (Al). With the increase of the Al content, a decrease in the values of magnetic entropy is observed. The magnitude of the isothermal magnetic entropy (|∆SM|) at the Tc decreases from 1.8 J/kg·K for x = 0 to 0.58 J/kg·K for x = 3 for a field change 14 kOe. Respectively, the relative cooling power (RCP) decreases with increasing Al content reaching 42 Jkg−1 for x = 0 to 28 Jkg−1 for x = 3.
| Reference Key |
jemmali2017crystalseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;M. Jemmali;S. Alleg;E. Dhahri;L. Bessais |
| Journal | turk kardiyoloji dernegi arsivi |
| Year | 2017 |
| DOI |
10.3390/cryst7060156
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.