influence of sintering temperature on crystallization behavior of cordierite synthesized from non-stoichiometric formulation
Clicks: 171
ID: 225657
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
171 views
20 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #140 of 435 articles by views in acta botânica brasílica
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 435 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Cordierite body with formulation of non-stoichiometric composition (2.5 MgO. 1.8 Al2O3. 5 SiO2) was synthesized using conventional techniques with standard raw materials. The sintering and crystallization behavior of the compositions was observed by Differential Thermal Analysis and Thermogravimetric Analysis (DTA/TG). The sequence of reaction and phase transformation was analyzed using X-ray Diffraction (XRD) technique and Rietveld structural refinement after sintering the samples at different temperature regarding the information from the DTA. The Scanning electron microscopy (SEM) was employed for morphology analysis. The DTA curve shows the crystallization temperature, Tc occur at 1259°C.Rietveld quantitative phase analysis results reveal that α phase Cordierite constitutes up to 96.4 wt% when the samples was sintered for 2 hours at the optimal temperature of 1375°C. The SEM micrograph revealed that the sample was heat treated at 1375°C obtained densified body with well alignment of crystal structure.
| Reference Key |
k.2016matecinfluence
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Eing K. K.;Johar B.;Ho L. N.;Zabar Y. |
| Journal | acta botânica brasílica |
| Year | 2016 |
| DOI |
10.1051/matecconf/20167801099
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.