estudio del mecanismo de compensación de batio₃ dopado con la₂o₃

In this work, the incorporation of several concentrations of the La3+ ion into the BaTiO3 lattice was studied. It was verified that low La3+ concentrations inhibits the grain growth and produces a highly densified material. However, a delay in the sintering behavior in ceramics with high doping concentrations was observed. The La3+ donor incorporation in the BaTiO3 modified the defects structure, favored titanium vacancies formation, and stabilized a pseudocubic phase. This effect influences the dielectric properties and the cubic-tetragonal transition temperature.

En este trabajo se estudió la incorporación del ión La3+ en la red de BaTiO3. Se comprobó que bajas concentraciones de La3+ inhiben el crecimiento de los granos de BaTiO3 significativamente, a la vez que originan un material altamente densificado. Sin embargo, se confirmó que existe un límite de concentración de La2O3 a partir del cual se observó un retardo en el sinterizado del BaTiO3. La incorporación de La3+ como donor en el BaTiO3 modificó su estructura de defectos, favoreció la formación de vacantes de titanio y lo estabilizó en una fase pseudocúbica. Este efecto también se refleja en las propiedades dieléctricas del material y en la temperatura de transición de fases cúbica-tetragonal.