in-situ synthesis of wc-co composite in wo3- co3o4- c system by carbothermic reduction method
Clicks: 187
ID: 208770
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
187 views
17 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #18 of 30 articles by views in journal of non-crystalline solids
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The aim of this investigation is obtaining WC-Co composite powder from WO3 and Co3O4 by in-situ and carbothermic reduction method using activated carbon as a reducing agent. In this study, cobalt and tungsten oxide powders with 17% carbon (30% more than stoichiometric value) were mixed by ball-milling under atmosphere of argon for 20 hours. Differential Thermal Analysis (DTA) and Thermal Gravimetric Analysis (TGA) results on powder mixture show complete reducing of oxides at 1050°C and forming cobalt carbide and tungsten carbide. Compact samples underwent carbothermic reduction at 1050 °C for different times of 1, 2 and 4 hours with protective layer of alumina and carbon powder mixture with ratio of 1:1. Based on X-Ray Diffraction (XRD) analyses, the best holding time in furnace is 4 hours, in which tungsten reduction and carbonization is completed. XRD evaluation of reduced compacted samples in three conditions of atmosphere protective layer of alumina and carbon powder mixture with ratio of 1:1, protective foil of refractory steel and argon, shows that unreduced oxides and extra phases are present in argon atmosphere and protective foil of steel but not in alumina and carbon mixture layer. The measurement results of physical and mechanical properties on the sintered composite sample in heating rate of 5 °C /min to temperature 1500 °C and the holding time of 2 hours under a shielding layer of alumina and carbon shows obtaining the optimal properties (Pr=80%, KIC=8.1 MPa , MHV=15.67GPa) comparable to that of advanced and costly methods.
| Reference Key |
moghaddam2017journalin-situ
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;A. Amiri Moghaddam;M. kalantar |
| Journal | journal of non-crystalline solids |
| Year | 2017 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.