compound formation and microstructure of as-cast high entropy aluminums
Clicks: 169
ID: 207523
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
169 views
27 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #110 of 136 articles by views in seminars in cancer biology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 136 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The aim of this work is to study the microstructure of four high entropy alloys (HEAs) produced by large scale vacuum die casting. Al40Cu15Mn5Ni5Si20Zn15, Al45Cu15Mn5Fe5Si5Ti5Zn20, Al35Cu5Fe5Mn5Si30V10Zr10, and Al50Ca5Cu5Ni10Si20Ti10 alloys formed a mixture of different structures, containing intermetallic compound (IC) and solid solution (SS) phases. The phases observed in the casting alloys were compared with the equilibrium phases predicted by Thermo-Calc. The measured densities varied from 3.33 g/cm−3 to 5.07 g/cm−3 and microhardness from 437 Hv to 887 Hv. Thus, the microhardness and estimated strength/density ratios are significantly higher than other lightweight high entropy alloys (LWHEAs).
| Reference Key |
sanchez2018metalscompound
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Jon Mikel Sanchez;Iban Vicario;Joseba Albizuri;Teresa Guraya;Natalia E. Koval;Jose Carlos Garcia |
| Journal | seminars in cancer biology |
| Year | 2018 |
| DOI |
10.3390/met8030167
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.