separation of rhenium from lead-rich molybdenite concentrate via hydrochloric acid leaching followed by oxidative roasting
Clicks: 195
ID: 204539
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
195 views
18 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #88 of 136 articles by views in seminars in cancer biology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 136 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Lead-rich molybdenite is a typical rhenium-bearing molybdenum resource in China, which has not been efficiently utilized due to its high contents of lead and gangue minerals. In this study, hydrochloric acid was used for preliminarily removing lead and calcite from a lead-rich molybdenite concentrate. Oxidative roasting-ammonia leaching was then carried out for separation of rhenium and extraction of molybdenum. The hydrochloric acid leaching experiments revealed that 93.6% Pb and 97.4% Ca were removed when the leaching was performed at 95 °C for 10 min with HCl concentration of 8 wt. % and liquid-solid ratio of 5 (mL/g). The results of direct oxidative roasting indicated that 89.3% rhenium was volatilized from the raw concentrate after roasting at 600 °C for 120 min in air. In contrast, the rhenium volatilization was enhanced distinctly to 98.0% after the acid-leached concentrate (leaching residue) was roasted at 550 °C for 100 min. By the subsequent ammonia leaching, 91.5% molybdenum was leached out from the calcine produced from oxidative roasting of the acid-leached concentrate, while only 79.3% Mo was leached from the calcine produced by roasting molybdenite concentrate without pretreatment.
| Reference Key |
li2016metalsseparation
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Guanghui Li;Zhixiong You;Hu Sun;Rong Sun;Zhiwei Peng;Yuanbo Zhang;Tao Jiang |
| Journal | seminars in cancer biology |
| Year | 2016 |
| DOI |
10.3390/met6110282
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.