leaching kinetics of hemimorphite in ammonium chloride solution
Clicks: 87
ID: 180628
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
25.8
/100
87 views
17 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #130 of 136 articles by views in seminars in cancer biology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 136 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The leaching kinetics of hemimorphite (Zn4Si2O7(OH)2·H2O) in ammonium chloride solution was presented in detail. Effects of stirring speed (150–350 rpm), leaching temperature (75–108 °C), particle size of hemimorphite (45–150 μm), and the concentration of ammonium chloride (3.5–5.5 mol/L) on the zinc extraction rate were studied. The zinc extraction rate enhanced slightly with the increase in stirring speed, but increased significantly with an increase in the leaching temperature and ammonium chloride concentration. Zinc extraction was enhanced significantly in the first 60 min with decreasing particle size, but had little effect on the leaching process after 60 min. Scanning electron microscopy (SEM) analysis showed that some silica gel formed in the leaching process was not separated from the hemimorphite surface, but covered some of the active particle surface. The Elovich equation successfully described the leaching kinetics of hemimorphite in ammonium chloride solution with an apparent activation energy of 405.14 kJ/mol at temperatures of 75–90 °C and 239.61 kJ/mol at temperatures of 95–108 °C, which is characteristic for a chemically-controlled process. Silica gel is generated at temperatures of 75–90 °C and decomposed into silica at temperatures of 95–108 °C.
| Reference Key |
zhao2017metalsleaching
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Duoqiang Zhao;Shenghai Yang;Yongming Chen;Chaobo Tang;Jing He;Hao Li |
| Journal | seminars in cancer biology |
| Year | 2017 |
| DOI |
10.3390/met7070237
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.