laboratory assessment of select methods of corrosion control and repair in reinforced concrete bridges
Clicks: 120
ID: 175715
2014
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
120 views
19 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #321 of 341 articles by views in Food chemistry
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 341 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Fourteen reinforced concrete laboratory test specimens were used to evaluate a number of corrosion control (CoC) procedures to prolong the life of patch repairs in corrosion-damaged reinforced concrete. These specimens included layered mixed-in chlorides to represent chloride contamination due to deicing salts. All specimens were exposed to accelerated corrosion testing for three months, subjected to patch repairs with various treatments, and further subjected to additional three months of exposure to accelerated corrosion. The use of thermal sprayed zinc, galvanic embedded anodes, epoxy/polyurethane coating, acrylic coating, and an epoxy patch repair material was evaluated individually or in combination. The specimens were assessed with respect to corrosion currents (estimated mass loss), chloride ingress, surface rust staining, and corrosion of the reinforcing steel observed after dissection. Results indicated that when used in patch repair applications, the embedded galvanic anode with top surface coating, galvanic thermal sprayed zinc, and galvanic thermal sprayed zinc with surface coating were more effective in controlling corrosion than the other treatments tested.
| Reference Key |
pritzl2014internationallaboratory
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Matthew D. Pritzl;Habib Tabatabai;Al Ghorbanpoor |
| Journal | Food chemistry |
| Year | 2014 |
| DOI |
10.1155/2014/175094
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.