Thermal degradation and pollutant emission from waste printed circuit boards mounted with electronic components.

Clicks: 282
ID: 17456
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #134 of 357 articles by views in Journal of hazardous materials

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 357 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
Waste printed circuit boards mounted with electronic components (WPCB-ECs) are generated from electronic waste dismantling and recycling process. Air-borne pollutants, including particulate matter (PM) and volatile organic compounds (VOCs), can be released during thermal treatment of WPCB-CEs. In this study, organic substances from WPCB-ECs were pyrolyzed by both thermo-gravimetric analysis (TGA) and in a quartz tube furnace. We discovered that board resin and solder coating were degraded in a one-stage process, whereas capacitor scarfskin and wire jacket had two degradation stages. Debromination of brominated flame retardants occurred, and HBr and phenol were the main products during TGA processing of board resin. Dehydrochlorination occurred, and HCl, benzene and toluene were detected during the pyrolysis of capacitor scarfskin. Benzene formation was found only in the first degradation stage (272-372 °C), while toluene was formed both in the two degradation stages. PM with bimodal mass size distributions at diameters of 0.45-0.5 and 4-5 μm were emitted during heating WPCB-ECs. The PM number concentrations were highest in the size ranges of 0.3-0.35 μm and 1.6-2 μm. The research produced new data on pollutant emissions during thermal treatment of WPCB-ECs, and information on strategies to prevent toxic exposures that compromise the health of recyclers.
Reference Key
guo2019thermaljournal Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Guo, Jie;Luo, Xiaomei;Tan, Shufei;Ogunseitan, Oladele A;Xu, Zhenming;
Journal Journal of hazardous materials
Year 2019
DOI
S0304-3894(19)30992-6
URL
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.