friction stir welding of super duplex stainless steel of uns s32750, its microstructure evaluation, mechanical and corrosion properties
Clicks: 197
ID: 165624
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
197 views
26 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #17 of 30 articles by views in journal of non-crystalline solids
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Super duplex stainless steel is a kind of duplex stainless steel that has pitting resistant equivalent number over than 40. Unified Numbering System (UNS) S32750 is a common super duplex stainless stee, that is mostly applied in oil and gas refinery industries, because of its proper corrosion-resistant properties . Therefore, joining of these steels by welding is very important, but the greatest problem in this regard is the corrosion and decrease in mechanical properties after welding.. In this research, UNS S32750has been joined by friction stir welding method. The tool being used in this research was a WC with 16mm shoulder diameter, 5 mm pin diameter, and 1.9 mm height. X-ray diffraction showed that harmful phases, such as sigma or chi have not been formed. Microstructure study indicated that grain size in the stir zone has decreased. Vickers Hardness Test Method has been applied on welded samples. Moderate microhardness of base metal was 285 Vickers but, the microhardness increased in the stir zone to 360 Vickers, because of decreasing the grain size. The cyclic polarization determined that potential and corrosion current of joint metal by friction stir welding method was similar to base metal. Also, it was revealed that ferrite percentage in the stir zone doesn't decrease very much because the friction stir welding heat input is very low and the colding rate is very high.
| Reference Key |
sarmadi2017journalfriction
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;M. Ahl Sarmadi;M. Shamanian;H. Edris;M. Atapoor;A. Behjat;M. Mohtadi Bonab;J. Szpunar |
| Journal | journal of non-crystalline solids |
| Year | 2017 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.