annealing of radiation-induced defects in burn-in stressed power vdmosfets
Clicks: 164
ID: 163350
2011
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
164 views
25 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #23 of 33 articles by views in postepy higieny i medycyny doswiadczalnej (online)
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The annealing of radiation-induced defects in burn-in stressed n-channel power VDMOSFETs with thick gate oxides (100 and 120 nm) is analysed. In comparison with the previous spontaneous recovery, the changes of device electrical parameters observed during annealing are highlighted by the elevated temperature and voltage applied to the gate, and are more pronounced in devices with a 120 nm thick gate oxide. The threshold voltage of VDMOSFETs with a 100 nm thick gate oxide during annealing has an initially slow growth, but then increases rapidly and reaches the value higher than the pre-irradiation one (rebound effect). In the case of devices with a 120 nm thick gate oxide, the threshold voltage behaviour also consists of a slight initial increase followed by a rapid, but dilatory increase, with an obvious tendency to achieve the rebound. The changes of channel carrier mobility during annealing are similar in all samples: at first, it slowly and then rapidly declines, and after reaching the minimum it begins to increase. In the case of VDMOSFETs with a thicker gate oxide, these changes are much slower. The underlying changes in the densities of gate oxide-trapped charge and interface traps are also delayed in devices with a thicker gate oxide. All these phenomena occur with certain delay in burn-in stressed devices compared to unstressed ones. The leading role in the mechanisms responsible for the observed phenomena is attributed to hydrogen related species.
| Reference Key |
m.2011nuclearannealing
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Đorić-Veljković Snežana M.;Manić Ivica Đ.;Davidović Vojkan S.;Danković Danijel M.;Golubović Snežana M.;Stojadinović Ninoslav D. |
| Journal | postepy higieny i medycyny doswiadczalnej (online) |
| Year | 2011 |
| DOI |
10.2298/NTRP1101018D
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.