microstructure, texture evolution and mechanical properties of vt3-1 titanium alloy processed by multi-pass drawing and subsequent isothermal annealing
Клики: 304
ID: 141866
2017
Метрики качества и эффективности статьи
Общее качество
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Вовлечённость читателей
Steady Performance
30.0
/100
304 просмотры
46 читатели
Оценка качества ИИ
Не проанализировано
Readership in this journal
SteadyRanked #26 of 136 articles by views in seminars in cancer biology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 136 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Аннотация
Microstructure, texture evolution, and mechanical properties of Ti–6Al–1.5Cr–2.5Mo–0.5Fe–0.3Si (VT3-1) titanium alloy processed by multi-pass drawing and subsequent isothermal annealing were systematically investigated. A fiber-like microstructure is formed after warm drawing at 760 °C with 60% area reduction. After isothermal annealing, the samples deformed to different amounts of area reduction show a similar volume fraction (80%) of α phase, while the sample deformed to 60% exhibits a homogeneous microstructure with a larger grain size (5.8 μm). The major texture component of α phase developed during warm drawing is centered at a position of {φ1 = 10°, φ = 65°, φ2 = 0°}. The textures for annealed samples are almost along the orientation of original deformation textures and show significant increases in orientation density and volume fraction compared with their deformed states. In addition, for the drawn samples, the ultimate tensile strength increases but the ductility decreases with increasing drawing deformation. A negative slope of yield strength of annealed samples versus grain size (d−1/2) is found due to the difference between texture softening for as-rolled + annealed state and texture hardening for drawn + annealed state. The mechanical properties of annealed samples are found to be strongly dependent on grain size and texture, resulting in the balance of the strength and ductility.
| Ссылочный ключ |
lei2017metalsmicrostructure,
Используйте этот ключ для автоцитирования в рукописи при использовании
SciMatic Manuscript Manager или Thesis Manager
|
|---|---|
| Авторы | ;Xiaofei Lei;Limin Dong;Zhiqiang Zhang;Yujing Liu;Yulin Hao;Rui Yang;Lai-Chang Zhang |
| Журнал | seminars in cancer biology |
| Год | 2017 |
| DOI |
10.3390/met7040131
|
| URL | |
| Ключевые слова |
Цитирования
Цитирования не найдены. Чтобы добавить цитирование, свяжитесь с администратором по адресу info@scimatic.org
Комментарии
Комментариев пока нет. Будьте первым, кто прокомментирует эту статью.