constitutive modelling and hot workability analysis by microstructure examination of gh4169 alloy
Clicks: 281
ID: 137997
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.2
/100
281 views
46 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #24 of 88 articles by views in turk kardiyoloji dernegi arsivi
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The relationships between hot deformation parameters and flow behaviour have attracted many researchers’ attention for the past few decades, whilst precise constitutive modelling of GH4169 remained a problem, which seriously affected the process and microstructure control of alloys. In this work, a modified Arrhenius type model was introduced to describe the flow stresses of various compression conditions. The model showed high precision in flow stress prediction. In order to facilitate workability evaluation for engineering applications, the hot processing maps were established at the strain of 0.4~0.6. The processing maps revealed an instability domain at 900~950 °C and 0.1~1 s−1, a high dissipation efficiency domain at 1060~1100 °C and 0.001~0.01 s−1, and a stable deformation domain for the rest of processing parameters. Microstructures of each domain were observed via optical microscope (OM) and electron backscattered diffraction (EBSD). The intriguing finding was that the microstructures morphology agreed well with the descriptions in “discontinuous mechanism”, and incompletely recrystallized microstructures were found in the instability domain. Fully recrystallized microstructures were found in the stable deformation domain, and grain coarsen in the high dissipation efficiency domain. Optimal hot working conditions were suggested based on the microstructure analysis. This investigation contributed to a comprehensive understanding of the workability of GH4169.
| Reference Key |
chen2018crystalsconstitutive
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Rongchuang Chen;Zhizhen Zheng;Jianjun Li;Fei Feng |
| Journal | turk kardiyoloji dernegi arsivi |
| Year | 2018 |
| DOI |
10.3390/cryst8070282
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.