poly(urethane-siloxane)s based on hyperbranched polyester as crosslinking agent: synthesis and characterization
Clicks: 283
ID: 131292
2012
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
283 views
58 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #34 of 151 articles by views in meditsinskaia radiologiia
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 151 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
A series of novel polyurethane crosslinked structures (PUs) was prepared from α,ω-dihydroxy-(ethylene oxide-poly(dimethylsiloxane)-ethylene oxide) (EO-PDMS-EO), 4,4’-methylenediphenyl diisocyanate and Boltorn® hyperbranched polyester of the third pseudo generation. The hydroxyfunctional hyperbranched aliphatic polyester with 26 end groups was used as crosslinking agent. In order to improve the compatibility of all reactants during the synthesis, PU samples were prepared by a step-growth polymerization in two stages in solution. The soft EO-PDMS-EO segment content was varied in the range from 15 to 40 wt.%. The influence of the EO-PDMS-EO content on the swelling behavior, crosslinking density, hardness, thermal and surface properties of the synthesized PUs was investigated. The structure of the synthesized polyurethanes was confirmed by the presence of specific bands in Fourier transform infrared spectra. Swelling studies were carried out to determine the crosslinking density and polyurethane networks with lower EOPDMS- EO content revealed higher crosslinking density. The glass transition temperature of the synthesized PUs, determined by differential scanning calorimetry, slightly increased from 50 to 58°C by decreasing EO-PDMS-EO content as a consequence of higher crosslinking density of samples. The increase of EO-PDMS-EO content leads to the better thermal stability, as it was confirmed by the value of the starting temperature of thermal degradation. The surface of the polyurethane networks became more hydrophobic with increasing EO-PDMS-EO content. The surface morphology of synthesized polyurethanes was analyzed by scanning electron microscopy.
| Reference Key |
v.2012journalpoly(urethane-siloxane)s
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Pergal Marija V.;Džunuzović Jasna V.;Ostojić Sanja;Pergal Miodrag M.;Radulović Aleksandra;Jovanović Slobodan |
| Journal | meditsinskaia radiologiia |
| Year | 2012 |
| DOI |
10.2298/JSC111013006P
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.