Ultrasound-assisted Li/Na co-intercalated exfoliation of graphite into few-layer graphene.

In this work, we developed a novel approach for few-layer graphene by employing Li/Na co-intercalated exfoliation assisted by ultrasound method. The experiments were conducted under the ultrasonic power of 300 W and the frequency of 40 kHz without the participation of any organic solvent. The effect of Li/Na proportion on the exfoliation of graphite was intensively investigated. The structure and morphology of the as-exfoliated graphene nanosheets (UGN) was determined by a series of characterizations. The results showed that the thicknesses of the as-exfoliated graphene nanosheets were about 2.38-2.56 nm (about 7-8 layers) at the optimal Li/Na ratio. The potential application of the as-exfoliated graphene nanosheets as additive in grease was evaluated by four-ball friction tester. The results demonstrated that the antifriction and antiwear performances of the grease with 0.06 wt% graphene were significantly improved by 21.35% and 30.32% relative to pure grease, respectively. The friction mechanism was proposed by detecting the worn surfaces.