fabrication and sintering behavior of er:srf2 transparent ceramics using chemically derived powder
Clicks: 183
ID: 165708
2018
In this paper, we report the fabrication of high-quality 5 at. % Er3+ ions doped SrF2 transparent ceramics, the potential candidate materials for a mid-infrared laser-gain medium by hot-pressing at 700 °C for 40 h using a chemically-derived powder. The phase structure, densification, and microstructure evolution of the Er:SrF2 ceramics were systematically investigated. In addition, the grain growth kinetic mechanism of Er:SrF2 was clarified. The results showed lattice diffusion to be the grain growth mechanism in the Er:SrF2 transparent ceramic of which highest in-line transmittance reached 92% at 2000 nm, i.e., very close to the theoretical transmittance value of SrF2 single crystal. Furthermore, the emission spectra showed that the strongest emission band was located at 2735 nm. This means that it is possible to achieve a laser output of approximately 2.7 μm in the 5 at. % Er3+ ions doped SrF2 transparent ceramics.
Reference Key |
liu2018materialsfabrication
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
---|---|
Authors | ;Jun Liu;Peng Liu;Jun Wang;Xiaodong Xu;Dongzhen Li;Jian Zhang;Xinming Nie |
Journal | Nature Materials |
Year | 2018 |
DOI | 10.3390/ma11040475 |
URL | |
Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.