Effect of Prior Rolling on Microstructures and Property of Diffusion-Bonded Mg/Al Alloy
Clicks: 189
ID: 94725
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
189 views
21 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #35 of 45 articles by views in advances in materials science and engineering
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
In this study, magnesium alloy AZ91, which was cast by double roll casting system, was rolled by a rolling mill. Then, rolled magnesium alloy and magnesium alloy without being rolled were, respectively, welded with aluminum alloy 6061 by diffusion bonding method. Furthermore, annealing process was applied to refine the microstructure and improve mechanical property. The microstructure and elemental distribution of diffusion zone were investigated with a scanning electron microscope (SEM), an electron probe micro analyzer (EPMA), and a transmission electron microscope (TEM). In addition, hardness and tensile strength were measured. When cast magnesium alloy was used, the width of diffusion layers was wider than that with rolled magnesium alloy. And the width increased with the increasing annealing temperatures. Element distribution of specimens with annealing was more uniform than that did not undergo annealing process. Furthermore, tensile strength turns to be strongest after annealing at 250°C. And the strength of the specimens with rolled magnesium alloy was stronger than that with cast magnesium alloy which was not rolled.
| Reference Key |
ding2019effectadvances
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Ding, Yunlong;Shi, Jialian;Ju, Dongying; |
| Journal | advances in materials science and engineering |
| Year | 2019 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.