Effects of Solidification Pressure and Heat Treatment on the Microstructure and Micro-Hardness of AlSi9CuMg Alloy.

Clicks: 347
ID: 84390
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #101 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The effect of high pressure (135 MPa) and the following heat treatment on the microstructure and micro-hardness of the squeezing cast AlSi9CuMg alloy is investigated, using optical microscopy (OM), Vickers tester, scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results indicate that the application of high pressure can increase under-cooling and the cooling rate during solidification and cause the refinement of the microstructure. The enhanced melt flow resulting from high pressure can also break the dendrite to form the spherical and elliptical primary α (Al) grains during the early stage of solidification. The winter-sweet flower-shaped primary α (Al) phases can also be formed through plastic deformation caused by the flow of the partially solidified melt. The ageing treatment results showed that a maximum (peak) micro-hardness value was obtained for each of the three ageing temperatures at different ageing times, and the highest peak value was achieved at 175 °C for 480 min. The micro-hardness change of the sample under different ageing processes was attributed to the variation of type, density, and size of the precipitates.
Reference Key
wei2019effectsmaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Wei, Lijun;Han, Baoshuai;Ye, Fan;Xu, Yanjin;Wu, Sujun;
Journal Materials (Basel, Switzerland)
Year 2019
DOI
E2229
URL
Keywords
high pressure strengthening solid solution melt flow squeezing casting

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.