Dynamic Fracture Toughness of TaC/CNTs/SiC CMCs Prepared by Spark Plasma Sintering
Clicks: 322
ID: 84280
2015
Article Quality & Performance Metrics
Overall Quality
Improving Quality
0.0
/100
Combines engagement data with AI-assessed academic quality
Reader Engagement
Emerging Content
6.9
/100
23 views
23 readers
Trending
AI Quality Assessment
Not analyzed
Abstract
This study focuses on the fracture toughness of TaC and carbon nanotubes (CNTs) reinforced SiC ceramic matrix composites (CMCs), prepared by spark plasma sintering (SPS) technique. A high densification of 98.4% was achieved under the sintering parameter of 133°C/min, 1800°C, and 90 MPa pressure. Vickers indentation was employed to measure the indentation toughness on the polished surface of ceramic samples, SEM was applied to directly observe the crack propagation after indentation, and split Hopkinson pressure bar (SHPB) was developed to determine the dynamic fracture toughness within the ceramic samples subjected to an impact in a three-point bending configuration.
| Reference Key |
xie2015dynamicadvances
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Xie, Qiaoyun;Wosu, Sylvanus N.; |
| Journal | advances in materials science and engineering |
| Year | 2015 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Materials of engineering and construction. Mechanics of materials
Engineering (General). Civil engineering (General)
Mechanical engineering and machinery
motor vehicles. aeronautics. astronautics
engineering geology. rock mechanics. soil mechanics. underground construction
structural engineering (general)
|
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.