Effect of Micro-Scale Er on the Microstructure and Fluidity of ZL205A Alloy.

Clicks: 245
ID: 81837
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #458 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The effect of Er addition on the fluidity and microstructure transformation of the as-cast and T5 heat-treated ZL205A alloys was investigated by optical microscope (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). The fluidity of the liquid metal after adding Er was tested and the fracture characteristics of the material were analyzed. The results indicated that Er was mainly dissolved into an α-Al matrix near the grain boundaries (GBs). It is easily segregated and enriched in the intersection of the GBs or the interface between the α and θ phase, which caused the intermetallic compounds to be distributed along the GBs to the neck and to fuse. Er could also inhibit the diffusion of Cu atoms in the process of solid solution, so that increased the residual eutectic structures in the crystal, while accelerating the precipitation progress of the Guinier-Preston (GP) zone and θ' phase and increasing precipitation of the θ phase. A small amount of precipitation of θ phase and micro-scale Er (0.1-0.5 wt %) can significantly increase the fluidity and reduce the casting defects, which can effectively improve the castability of the ZL205A alloy. The interface between the (AlCuEr) phase and matrix is the main area of microcracks, through analyzing the fracture morphology.
Reference Key
guo2019effectmaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Guo, Tingbiao;Wang, Bing;Zhang, Zhanfei;Sun, Quanzhen;Jin, Yuhua;Ding, Wanwu;
Journal Materials (Basel, Switzerland)
Year 2019
DOI
E1688
URL
Keywords
microstructure t5 heat treatment zl205a fluidity rare earth er flavonoid vasorelaxation zingiberaceae boesenbergia rotunda 4-hydroxypanduratin

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.