Influence of Polyurea Composite Coating on Selected Mechanical Properties of AISI 304 Steel.

Clicks: 379
ID: 56109
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #51 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
This paper contains experimental results of mechanical testing of the AISI 304 steel with composite coatings. The main goal was to investigate the impact of the applied polyurea composite coating on selected mechanical properties: Adhesion, impact resistance, static behavior, and, finally, fatigue lifetime of notched specimens. In the paper the following configurations of coatings were tested: EP (epoxy resin), EP_GF (epoxy resin + glass fabric), EP_GF_HF (epoxy resin + glass fabric hemp fiber), EP_PUA (epoxy resin + polyurea) resin, EP_GF_PUA (epoxy resin + glass fabric + polyurea) resin, and EP_GF_HF_PUA (epoxy resin + glass fabric + hemp fiber + polyurea) resin. The highest value of force required to break adhesive bonds was observed for the EP_PUA coating, the smallest for the single EP coating. A tendency of polyurea to increase the adhesion of the coating to the base was noticed. The largest area of delamination during the impact test was observed for the EP_GF_HF coating and the smallest for the EP-coated sample. In all tested samples, observed delamination damage during the pull-off test was located between the coating and the metallic base of the sample.
Reference Key
duda2019influencematerials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Duda, Monika;Pach, Joanna;Lesiuk, Grzegorz;
Journal Materials (Basel, Switzerland)
Year 2019
DOI
E3137
URL
Keywords
fatigue adhesion delamination polyurea aisi 304 composite coating impact resistance

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.