Bending shape memory behaviours of carbon fibre reinforced polyurethane-type shape memory polymer composites under relatively small deformation: Characterisation and computational simulation.

Clicks: 444
ID: 54278
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #2 of 41 articles by views in Journal of the mechanical behavior of biomedical materials

Most read Least read

Bar heights use a square-root scale.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
Shape memory polyurethanes (SMPU) have been of great interest in biomedical applications because of their unique ability to recover a primary shape by external actuation. This advantage can allow for easy suture and minimum tissue damage caused by surgery. Since SMPU suffer from low stiffness and low strength, carbon fibres have been widely used to reinforce SMPU, and their shape memory properties have been investigated using thermomechanical tensile tests. In reality, however, bending situations are more common than tensile situations, such as human skulls. In this study, carbon fibre reinforced SMPU (CF/SMPU) composites were studied as promising cranial implants that can offer shape memory properties, shape flexibility and high strength. First, the basic properties of pristine SMPU and CF/SMPU composites were characterised, including glass transition temperature (T), the viscosity of SMPU, the morphology of CF/SMPU, and their tensile and flexural mechanical properties. Then, a new method using rheometer was developed to study the shape memory behaviours of SMPU and CF/SMPU with three-point bending under relatively small deformations (≤1%), including flexural stress during programming and cooling, and bending recovery force during shape recovery. Finally, due to the invisibility of recovery process that was conducted in an enclosed temperature-controlling chamber of rheometer, the finite element method (FEM) was used to simulate the bending recovery test. The results showed carbon fibres significantly enhanced the mechanical properties (Young's modulus and flexural modulus) of SMPU. In terms of bending shape recovery, compared to pristine SMPU, CF/SMPU composites obtained substantially higher flexural stress during programming and cooling processes, and larger, more stable recovery force during recovery. The FEM results consolidated the peak recovery force of SMPU and the continuously growing recovery force of CF/SMPU as the temperature increased. Our findings on the improved mechanical and shape memory properties can provide a solid foundation for the potential applications of CF/SMPU composites as cranial implants.
Reference Key
cheng2019bendingjournal Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Cheng, Xinying;Chen, Yuan;Dai, Shaocong;Bilek, Marcela M M;Bao, Shisan;Ye, Lin;
Journal Journal of the mechanical behavior of biomedical materials
Year 2019
DOI
S1751-6161(19)30641-1
URL
Keywords
polyurethane bending shape recovery carbon fibre cranial implants shape memory polymer

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.