Critical Issues of Double-Metal Layer Coating on FBG for Applications at High Temperatures.

Clicks: 222
ID: 40358
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #1,217 of 1,694 articles by views in sensors

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 1,694 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
Use of fiber Bragg gratings (FBGs) to monitor high temperature (HT) applications is of great interest to the research community. Standard commercial FBGs can operate up to 600 ∘ C. For applications beyond that value, specific processing of the FBGs must be adopted to allow the grating not to deteriorate. The most common technique used to process FBGs for HT applications is the regeneration procedure (RP), which typically extends their use up to 1000 ∘ C. RP involves a long-term annealing of the FBGs, to be done at a temperature ranging from 550 to 950 ∘ C. As at that temperature, the original coating of the FBGs would burn out, they shall stay uncoated, and their brittleness is a serious concern to deal with. Depositing a metal coating on the FBGs prior to process them for RP offers an effective solution to provide them with the necessary mechanical strengthening. In this paper, a procedure to provide the FBG with a bimetallic coating made by copper and nickel electrodeposition (ED) is proposed, discussing issues related to the coating morphology, adherence to the fiber, and effects on the grating spectral response. To define the processing parameters of the proposed procedure, production tests were performed on dummy samples which were used for destructive SEM-EDS analysis. As a critical step, the proposed procedure was shown to necessitate a heat treatment after the nickel ED, to remove the absorbed hydrogen. The spectral response of the FBG samples was monitored along the various steps of the proposed procedure and, as a final proof test for adherence stability of the bimetallic coating, along a heating/cooling cycle from room temperature to 1010 ∘ C. The results suggest that, given the emergence of Kirkendall voids at the copper-nickel interface, occurring at the highest temperatures (700-1010 ∘ C), the bimetallic layer could be employed as FBG coating up to 700 ∘ C.
Reference Key
lupi2019criticalsensors Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Lupi, Carla;Felli, Ferdinando;dell'Era, Alessandro;Ciro, Erwin;Caponero, Michele Arturo;Kalinowski, Hypolito José;Vendittozzi, Cristian;
Journal sensors
Year 2019
DOI
E3824
URL
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.