Primary Crystal Orientation of the Thin-Walled Area of Single-Crystalline Turbine Blade Airfoils.

Clicks: 196
ID: 39019
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #586 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The thin-walled airfoil areas of as-cast single-crystalline turbine blades made of CMSX-4 superalloy were studied. The blades were produced by the industrial Bridgman technique at withdrawal rates of 2, 3 and 4 mm/min. The angle between the [001] crystallographic direction and blade axis, related to the primary orientation, was defined by the Ω-scan X-ray diffraction method at points on the camber line located near the tip of an airfoil and at points of a line located in parallel and near the trailing edge. Additionally, primary crystal orientation was determined by Laue diffraction at the selected points of an airfoil. The influence of mould wall inclination on the primary crystal orientation of the thin-walled areas is discussed. The effect of change in the [001] crystallographic direction, named as "force directing", was considered with regard to the arrangement of primary dendrite arms in relation to the trailing edge and the camber line. It was stated that when the distance between the mould walls is less than the critical value of about 1.5 mm the "force directing" increases as the distance between the walls of the mould decreases. The effect may be controlled by selecting an appropriate secondary orientation using a seed crystal in the blade production process. The model of dendrite interaction with the mould walls, including bending and "deflection", was proposed.
Reference Key
bogdanowicz2019primarymaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Bogdanowicz, Włodzimierz;Krawczyk, Jacek;Paszkowski, Robert;Sieniawski, Jan;
Journal Materials (Basel, Switzerland)
Year 2019
DOI
E2699
URL
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.