Influence of Temperature on the Longitudinal Cracking in Multipurpose Precast Concrete Sleepers Prior to Their Installation.

Clicks: 212
ID: 37070
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #548 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
Prestressed monoblock railway sleepers are concrete elements with almost no reinforcement apart from the prestressing wires, which makes them very sensitive to any stress variation that can induce tensile stresses. In recent years, severe longitudinal cracking has been observed in a number of sleepers in hot regions of Spain, even before these elements were put in service. This work studies the problem while considering the thermal variation as the main factor affecting this cracking phenomenon. A non-linear static load-step analysis is applied on a non-linear finite element model to reproduce the problem and, after its experimental validation, the influence of three design parameters of the sleepers are studied: the nature of concrete aggregates, the dowel thickness, and the dowel material. The results show that all these three parameters may have significant influence on the problem, with the dowel material being the most important parameter. When the dowels are made of a material with a high elastic modulus and a high thermal expansion coefficient, the crack opening induced by a realistic thermal variation can reach significant values and result in longitudinal crack propagation. The changes of humidity are not considered in this study because they are beyond the scope of this work.
Reference Key
donairevila2019influencematerials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Donaire-Ávila, Jesús;Montañés-López, Antonio;Suárez, Fernando;
Journal Materials (Basel, Switzerland)
Year 2019
DOI
E2731
URL
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.