Magnetic Barkhausen emission for characterizing AISI 1045 steel plastically deformed

The aim of this work was to correlate parameters of the metallurgical structure such as size and reorganizing the grains, as well as the hardening capacity and the samples distortion of AISI 1045 steel plastically deformed by roll and then fractioned, with average values root means square RMS of a Barkhausen Emission. The analyzed samples were deformed by using forces of 500, 1500 and 2500 N, angular speed of 27, 54, and 110 r.p.m and tool advance of 0,075; 0,125 and 0,25 mm / rev. Then, they underwent a traction process using a CRITM DNS 200 machine, with a load of 200 kN. It was observed that the EMB signal presented an increasing performance in correspondence with the deformation decline and the increasing in tension and the hardness degree. The study of commercial steel AISI 1045 plastically deformed with roller and then pulled with EMB technique, allowed corroborating the potential of this technique as a non-destructive testing.