Effect of PDLA and Amide Compounds as Mixed Nucleating Agents on Crystallization Behaviors of Poly (l-lactic Acid)

Clicks: 244
ID: 31165
2018
Free PDF
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Emerging

Ranked #432 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The improvement of the rate of crystallization and crystallinity of poly (l-lactic acid) (PLLA) is one of the key performance elements for PLLA to perform better at the higher temperature than its heat deflection temperature (around 60 °C). The organic nucleating agent compounds are one of the interesting choice as they can offer the clarity of products. On the other hand, the nucleated PLLA can be prepared using a low molecular weight poly (d-lactic acid) (PDLA). The aim of this work was to explore the effect of an unsaturated amide compound and PDLA as single and mixed nucleating agents used for PLLA. The crystallization rate and kinetics were investigated and compared for the synthetic unsaturated amide compound (N,N′-ethylenebis (10-undecenamide) (EBU)) and commercial hydrazide compound (tetramethylenedicarboxylic dibenzoylhydrazide (TMC-306)). PLLA samples was prepared by melt-mixing with TMC or EBU incorporated with peroxide. The influence of different nucleating agents loading on thermal properties, crystallization behaviors, and rheological properties of PLLA were explored by differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). The results showed that the addition of EBU or TMC 0.5 phr could pronouncedly increase the crystallinity of PLLA from 3.80% to 24.84% and 8.61%, respectively. The crystallization peak appeared at 112.3 °C in the cooling scan at the rate 7 °C/min when addition EBU and peroxide into PLLA. This indicated that EBU acted as an efficient nucleating agent for PLLA. In isothermal crystallization run at 110 °C, it was found that the overall crystallization rate of nucleated PLLA with TMC or EBU was much faster than neat PLLA. The crystallization half-time indicated that the existence of TMC or EBU could slightly decrease to 2.90 and 1.96 min, respectively compared to neat PLLA (4.60 min). Finally, a low molecular weight PDLA with different contents between 3 and 7 wt % was added in PLLA with EBU and peroxide to investigate the effect of mixed nucleating agents. The crystallization rate of the incorporation of PDLA/EBU/peroxide into PLLA was discussed with the proposed crystallization mechanism. The results revealed the stereocomplex temperature peak at 207 °C as well as normal melting temperature of PLLA. The kinetics of growth crystallization, the crystallization half-time of PLLA at 110 °C was reduced from 4.60 min to 1.96 min (when adding EBU alone) and to 2.62 min (when using mixed PDLA and EBU).
Reference Key
khwanpipat2018effectmaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Khwanpipat, Thanawat;Seadan, Manus;Suttiruengwong, Supakij;
Journal Materials (Basel, Switzerland)
Year 2018
DOI
DOI not found
URL
http://www.mdpi.com/1996-1944/11/7/1139
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.