Development of steel fiber reinforced self-compacting concrete for high chloride environment
Clicks: 1
ID: 285097
2023
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
0.0
/100
1 views
0 readers
AI Quality Assessment
Not analyzed
Readership in this journal
Ranked #2,317 of 3,757 articles by views in Malay Journal
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 3,757 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Corrosion has been the leading cause of reinforced concrete structure degradation. Structures in marine environments are susceptible to accelerated corrosion due to the presence of chloride. Corrosion due to chloride attack is known to be fast and severe. Corrosion products are typically 3 to 6 times the volume of steel reinforcement, which can induce stress that will cause cracks. The rate of corrosion is affected by the permeability of concrete and its durability to prevent or at least delay the cracks. These ideas were capitalized on in improving the concrete's corrosion resistance. Self-compacting concrete was used as a reference because of its established advantages, such as low porosity and permeability due to its low water content and high cement factor, which improves the passivation of rebar. In order to improve the durability, steel fiber is added to the developed concrete. The addition of steel fiber improves the cracking resistance of concrete, and some of the steel fiber can be attached to the rebar, which redirects the flow of current and serves as a sacrificial anode in reference to the literature. Models derived based on material constituents (cement, w/c, SP, and steel fiber) predict the following responses, slump flow (R2=0.847), l-box (R2=0.626), gtm (R2=0.727), fc’ (R2=0.432), 5-day corrosion (R2=0.998), 15-day corrosion (R2=0.626). The cement ratio has been the leading factor that affects the responses with p-values of >0.05, 0.276, >0.05, 0.33, >0.05, and >0.05, respectively. Steel fiber has also been significant to most responses, including the corrosion level. The P-values calculated for each response were, 0.944, >0.05, 0.235, 0.0669, >0.05, and >0.05. The corrosion level of SFRSCC is lower by 45.41% by average as compared to SFRC design mixes. This research also successfully developed charts that can used as a substitute for the troubleshooting guide for design mix of SFRSCC. The optimal design mix was calculated using the derived models. Several criteria were set, such as, the mixture should yield acceptable rheological properties in accordance with EFNARC, the compressive strength should be greater than 28Mpa, and the corrosion level should be minimized. The optimum design mix has a projected 15-day corrosion level of 6.8%, which is lower than the lowest corrosion level from the data used. The derived optimum design mix has cement (469.76kg), w/c (0.4), SP (0.734%) and steel fiber (30%).
| Reference Key |
persistent_1760654612_68f1751466174
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Clemente, Stephen John C. |
| Journal | Malay Journal |
| Year | 2023 |
| DOI |
DOI not found
|
| URL | |
| Keywords | Keywords not found |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.