3D Porous MXene (Ti3C2Tx) Prepared by Alkaline-Induced Flocculation for Supercapacitor Electrodes
Clicks: 66
ID: 280674
2022
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
0.3
/100
66 views
1 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #758 of 812 articles by views in Materials (Basel, Switzerland)
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
2D layered MXene (Ti3C2Tx) with high conductivity and pseudo-capacitance properties presents great application potential with regard to electrode materials for supercapacitors. However, the self-restacking and agglomeration phenomenon between Ti3C2Tx layers retards ion transfer and limits electrochemical performance improvement. In this study, a 3D porous structure of Ti3C2Tx was obtained by adding alkali to a Ti3C2Tx colloid, which was followed by flocculation. Alkaline-induced flocculation is simple and effective, can be completed within minutes, and provides 3D porous networks. As 3D porous network structures present larger surface areas and more active sites, ions transfer accelerates, which is crucial with regard to the improvement of the superior capacitance and rate performance of electrodes. The sample processed with KOH (K-a-Ti3C2Tx) exhibited a high capacity of approximately 300.2 F g−1 at the current density of 1 A g−1. The capacitance of the samples treated with NaOH and LiOH is low. In addition, annealing is essential to further improve the capacitive performance of Ti3C2Tx. After annealing at 400 °C for 2 h in a vacuum tube furnace, the sample treated with KOH (K-A-Ti3C2Tx) exhibited an excellent specific capacitance of approximately 400.7 F g−1 at a current density of 1 A g−1, which is considerably higher than that of pristine Ti3C2Tx (228.2 F g−1). Furthermore, after 5000 charge–discharge cycles, the capacitance retention rate reached 89%. This result can be attributed to annealing, which can further remove unfavourable surface groups, such as –F or –Cl, and then improve conductivity capacitance and rate performance. This study can provide an effective approach to the preparation of high-performance supercapacitor electrode materials.
| Reference Key |
chen20223dmaterials
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Chen, Weihua;Tang, Jiancheng;Cheng, Peidong;Ai, Yunlong;Xu, Yi;Ye, Nan; |
| Journal | Materials (Basel, Switzerland) |
| Year | 2022 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.