Efficient Production of Segmented Carbon Nanofibers via Catalytic Decomposition of Trichloroethylene over Ni-W Catalyst.

Clicks: 170
ID: 276559
2023
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Emerging

Ranked #638 of 812 articles by views in Materials (Basel, Switzerland)

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The catalytic utilization of chlorine-organic wastes remains of extreme importance from an ecological point of view. Depending on the molecular structure of the chlorine-substituted hydrocarbon (presence of unsaturated bonds, intermolecular chlorine-to-hydrogen ratio), the features of its catalytic decomposition can be significantly different. Often, 1,2-dichloroethane is used as a model substrate. In the present work, the catalytic decomposition of trichloroethylene (CHCl) over microdispersed 100Ni and 96Ni-4W with the formation of carbon nanofibers (CNF) was studied. Catalysts were obtained by a co-precipitation of complex salts followed by reductive thermolysis. The disintegration of the initial bulk alloy driven by its interaction with the reaction mixture CHCl/H/Ar entails the formation of submicron active particles. It has been established that the optimal activity of the pristine Ni catalyst and the 96Ni-4W alloy is provided in temperature ranges of 500-650 °C and 475-725 °C, respectively. The maximum yield of CNF for 2 h of reaction was 63 g/g for 100Ni and 112 g/g for 96Ni-4W catalyst. Longevity tests showed that nickel undergoes fast deactivation (after 3 h), whereas the 96Ni-4W catalyst remains active for 7 h of interaction. The effects of the catalyst's composition and the reaction temperature upon the structural and morphological characteristics of synthesized carbon nanofibers were investigated by X-ray diffraction analysis, Raman spectroscopy, and electron microscopies. The initial stages of the carbon erosion process were precisely examined by transmission electron microscopy coupled with elemental mapping. The segmented structure of CNF was found to be prevailing in a range of 500-650 °C. The textural parameters of carbon product (S and V) were shown to reach maximum values (374 m/g and 0.71 cm/g, respectively) at the reaction temperature of 550 °C.
Reference Key
potylitsyna2023efficientmaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Potylitsyna, Arina R;Rudneva, Yuliya V;Bauman, Yury I;Plyusnin, Pavel E;Stoyanovskii, Vladimir O;Gerasimov, Evgeny Y;Vedyagin, Aleksey A;Shubin, Yury V;Mishakov, Ilya V;
Journal Materials (Basel, Switzerland)
Year 2023
DOI
845
URL
Keywords
nickel trichloroethylene carbon nanomaterials carbon nanofibers tungsten carbon erosion

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.