Postdeposition Annealing Effect on Cu2ZnSnS4 Thin Films Grown at Different Substrate Temperature
Clicks: 152
ID: 263609
2014
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
152 views
20 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #20 of 110 articles by views in international journal of photoenergy
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Cu2ZnSnS4 (CZTS) thin films were deposited on top of Molybdenum (Mo) coated soda lime glass (SLG) substrates using a single target rf magnetron sputtering technique. The sputtering parameters such as base pressure, working pressure, rf power, argon (Ar) gas flow rate, and deposition time were kept consistent throughout the experiment. The effect of different substrate temperatures, for example, room temperature (RT), 300°C, 350°C, 370°C, 400°C, and 450°C, was analyzed by studying their structural, electrical, and optical properties. As-sputtered films were then annealed at 460°C. X-ray diffraction (XRD) measurement revealed the structure to be kesterite with peak of (112) plane in both annealed and as-sputtered CZTS thin films. The crystallinity of the films improved with the increasing substrate temperature until 370°C. Secondary phases of MoS2, CuxMoSx, CuxSnSx, CuxS, and Cu6MoSnS8 (hemusite) were also observed in the annealed CZTS films. Scanning electron microscopy (SEM) shows crystallite size of deposited CZTS thin film to be proportionally related to deposition temperature. The highest surface roughness of 67.318 nm is observed by atomic force microscopy (AFM). The conductivity type of the films was found to be p-type by Hall effect measurement system.
| Reference Key |
nadi2014postdepositioninternational
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Nadi, Samia Ahmed;Chelvanathan, Puvaneswaran;Zakaria, Zaihasraf;Alam, Mohammad Mezbaul;Alothman, Zeid A.;Sopian, Kamaruzzaman;Amin, Nowshad; |
| Journal | international journal of photoenergy |
| Year | 2014 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.