fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels
Clicks: 385
ID: 260102
2011
Article Quality & Performance Metrics
Overall Quality
Improving Quality
0.0
/100
Combines engagement data with AI-assessed academic quality
Reader Engagement
Star Article
81.0
/100
381 views
306 readers
Trending
AI Quality Assessment
Not analyzed
Abstract
The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses.
| Reference Key |
song2011fratturafracture
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Kyongchan Song;Dawn R. Phillips;Norman F. Knight, Jr.;Ivatury S. Raju |
| Journal | applied catalysis |
| Year | 2011 |
| DOI |
DOI not found
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.