analysis of poly(lactic-co-glycolic acid)/poly(isoprene) polymeric blend for application as biomaterial
Clicks: 302
ID: 260055
2013
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
302 views
63 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #20 of 78 articles by views in journal of the chemical society, perkin transactions 1
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The application of renewable raw materials encourages research in the biopolymers area. The Poly(Lactic-co-Glycolic Acid)/Poly(Isoprene) (PLGA/IR) blend combines biocompatibility for application in the health field with excellent mechanical properties. The blend was obtained by solubilization of polymers in organic solvents. To investigate the polymer thermochemical properties, FTIR and DSC were applied. To investigate the composition's influence over polymer mechanical properties, tensile and hardness test were applied. To analyze the blends response in the cell environment, a stent was produced by injection molding process, and Cell Viability Test and Previous Implantability were used. The Infrared spectra show that chemical composition is related only with polymers proportion in the blend. The calorimetry shows a partial miscibility in the blend. The tensile test shows that adding Poly(Isoprene) to Poly(Lactic-co-Glycolic Acid) induced a relevant reduction in the Young modulus, tensile stress and tenacity of the material, which was altered from the fragile raw PLGA to a ductile material. The composition did not affect the blend hardness. The cell viability test shows that the blend has potential application as biomaterial, while the first results of implantability indicate that the polymeric stent kept its original position and caused low fibrosis.
| Reference Key |
marques2013polmerosanalysis
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Douglas Ramos Marques;Luis Alberto dos Santos;Luciano Ferraz Schopf;José Carlos Soares de Fraga |
| Journal | journal of the chemical society, perkin transactions 1 |
| Year | 2013 |
| DOI |
10.4322/polimeros.2013.099
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.