effect of the noble metals addition on the oxidation behavior of ni3al
Clicks: 123
ID: 259867
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.9
/100
123 views
11 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #187 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
This paper discusses the effect of the addition of noble metals on the microstructure, mechanism, and oxidation kinetics of the Ni3Al intermetallic alloy. Ni3Al was doped with 1% (atomic percent) of Au, Ag, Pd, and Pt. Oxidation behavior of the alloys was evaluated at 900, 1000, and 1100°C in O2 for 24 hours. XRD analysis showed that the addition of noble metals favored the oxide growth on preferential crystallographic planes. In addition, the preferential substitution of the noble metals in the Ni3Al structure modifies the surface composition by increasing the Al/Ni ratio. It was observed that most of the alloys showed a subparabolic behavior, and only the intermetallic base and the alloy doped with Ag show a parabolic behavior at 900°C. The developed oxides were analyzed both superficially and in cross section by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDXA). It was evident that only the intermetallic base showed the formation of a duplex oxide scale (Al2O3/NiO). The alloys doped with noble metals showed the oxide growth practically of pure Al2O3. This was due to a decrease in the diffusion of the Ni cations because of the presence of the noble metals in the crystalline structure.
| Reference Key |
ramos-hernandez2018advanceseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;J. J. Ramos-Hernandez;J. Porcayo-Calderon;J. G. Gonzalez-Rodriguez;Jan Mayén;G. Lara-Rodriguez;V. M. Salinas-Bravo;L. Martinez-Gomez |
| Journal | bulletin of the korean chemical society |
| Year | 2018 |
| DOI |
10.1155/2018/1616340
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.