characterization of oxide growth on surface of al-mg-si welded joint
Clicks: 6
ID: 250353
2014
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
1.5
/100
6 views
5 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #248 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Al-Mg-Si (AA6061) Al alloy plates were joined by the method of gas metal arc welding using Al-5Mg (ER5356) filler metal and were subjected to the oxidation test in flowing air environment at 600∘C from 8 to 40 hours and the weight gain was measured. The characteristic of oxide grown on welded zone surface was examined by SEM/EDS, XRD, and XPS. Oxide was observed to grow on the fused metal surface suggesting the possibility of modifying the oxide chemistry under high temperature environment. It was found that the oxidation behavior of fused metal affected by the nature of their oxide growth and morphology, was influenced by their welding process and the difference in the chemical composition.
| Reference Key |
jalar2014advancescharacterization
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Azman Jalar;Nur Azida Che Lah;Norinsan Kamil Othman;Roslinda Shamsudin;Abdul Razak Daud;Syed Roslee Sayd Bakar |
| Journal | bulletin of the korean chemical society |
| Year | 2014 |
| DOI |
10.1155/2014/272804
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.