synthesis and characterization of low loss dielectric ceramics prepared from composite of titanate nanosheets with barium ions
Clicks: 190
ID: 248467
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
190 views
39 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #143 of 443 articles by views in reproductive biology and endocrinology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 443 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
We report a strategy for preparing barium titanate precursor, being the composite of titanate nanosheets (TN) with barium ions (Ba-TN), which subjected to step sintering allows obtaining TiO2 rich barium titanate ceramics of stoichiometry BaTi4O9 or Ba2Ti9O20. These compounds are important in modern electronics due to their required dielectric properties and grains’ size that can be preserved in nanometric range. The morphology studies, structural characterization, and dielectric investigations were performed simultaneously in each step of Ba-TN calcinations in order to properly characterize type of obtained ceramic, its grains’ morphology, and dielectric properties. The Ba-TN precursor can be sintered at given temperatures, so that its dielectric permittivity can be tuned between 25 and 42 with controlled temperature coefficients that change from negative 32 ppm/°C for Ba-TN sintered at 900°C up to positive 37 ppm/°C after calcination at 1300°C. XRD analysis and Raman investigations performed for the Ba-TN in the temperature range of 900÷1250°C showed that below 1100°C we obtained as a main phase BaTi4O9, whereas the higher calcinations temperature transformed Ba-TN into Ba2Ti9O20. Taking into account trend of device miniaturization and nanoscopic size requirements, temperatures of 900°C and 1100°C seem to be an optimal condition for Ba-TN precursor calcinations that guarantee the satisfactory value of dielectric permittivity (ε=26 and 32) and ceramic grains with a mean size of ~180 nm and ~550 nm, respectively.
| Reference Key |
wypych-puszkarz2017journalsynthesis
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Aleksandra Wypych-Puszkarz;Izabela Bobowska;Angelika Wrzesinska;Agnieszka Opasinska;Waldemar Maniukiewicz;Piotr Wojciechowski;Jacek Ulanski |
| Journal | reproductive biology and endocrinology |
| Year | 2017 |
| DOI |
10.1155/2017/1351085
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.