effects of cellulosic base sheet pore structure and soybean oil-based polymer layer on cellulosic packaging performance as a barrier for water and water vapor
Clicks: 137
ID: 239051
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
137 views
18 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #167 of 185 articles by views in medical archives (sarajevo, bosnia and herzegovina)
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 185 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Cellulose-based materials are good alternatives to petroleum-based materials in the packaging industry, considering their sufficient mechanical properties and sustainability; however, the barrier performances of cellulosic packaging materials against water and water vapor are generally poor due to the hydrophilic nature of cellulose. In this study, a soybean oil-based polymer was synthesized on the surface of several cellulosic materials through an acrylated-epoxidized soybean oil (AESO) reactive coating. The best conversion of the reaction was observed when a suitable reaction temperature, curing time, initiator dosing, and monomer content were selected. Five different types of cellulosic packaging materials were used as substrates for the reactive coating, and their barrier performances were investigated. The improvement in water barrier properties was indicated by the change in water droplet contact angle (CA). The water vapor permeability (WVP) of the substrates was reduced significantly after coating. The water vapor barrier properties of the coating were highly dependent on the tested substrate. A comparison of CA and WVP showed that the change in water vapor barrier did not correspond to surface hydrophobicity.
| Reference Key |
lu2016bioresourceseffects
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Peng Lu;Xiaofei Tian;Yang Liu;Zhiwei Wang |
| Journal | medical archives (sarajevo, bosnia and herzegovina) |
| Year | 2016 |
| DOI |
10.15376/biores.11.4.8483-8495
|
| URL | |
| Keywords | Keywords not found |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.