enhanced oxidation resistance of polyphenylene sulfide composites based on montmorillonite modified by benzimidazolium salt
Clicks: 223
ID: 225352
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
223 views
19 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #135 of 194 articles by views in Journal of Fluorescence
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 194 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Organic montmorillonite (MMT) modified by 1,3-dihexadecyl-3H-benzimidazolium bromide (Bz) was used to prepare polyphenylene sulfide (PPS)/MMT composites by melting intercalation. The PPS/MMT composites showed mixed morphology, being comprised of exfoliated and intercalated structures with slight agglomerates. The tensile property of PPS/MMT composites was significantly improved due to the good dispersion of the MMT nanolayers. The test results showed that the tensile strength retention of PPS/MMT composites was higher than that of pure PPS after the oxidation treatment. Moreover, FTIR and XPS analyses were also used to evaluate the oxidation resistance of PPS composites. The FTIR analysis confirmed that adding MMT could better limit the damage of the C–S group and retard the generation of sulfuryl groups (–SO2–) during the oxidation treatment compared to pure PPS. The XPS analysis also suggested that the addition of MMT could reduce the chemical combination of the elements sulfur (S) and oxygen (O) during oxidation treatment. Furthermore, the MMT nanolayers could also promote the transfer of S from a C–S bond into an –SO2– group.
| Reference Key |
xing2018polymersenhanced
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Jian Xing;Zhenzhen Xu;Bingyao Deng |
| Journal | Journal of Fluorescence |
| Year | 2018 |
| DOI |
10.3390/polym10010083
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.