a numerical and experimental study through laser thermography for defect detection on metal additive manufactured parts
Clicks: 217
ID: 223724
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
217 views
30 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #19 of 46 articles by views in applied catalysis
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Additive manufacturing has been recently employed in industrial sectors with the fundamental requirement for zero defect parts. Technological developments in additive manufacturing notwithstanding, there continues to be a scarcity of non-destructive inspection techniques to be exploited during the manufacturing process itself, thus limiting industrial advancements and extensive applications. Therefore, being able to integrate the defect inspection phase within the additive manufacturing process would open the way to enabling corrective actions on the component in itinere, that is, before reaching the final product. For this reason, new methods of in-process monitoring are gaining more and more attention nowadays. In this work, a remote laser thermographic methodology is employed as a mean to detect micrometric defects in additive manufactured samples. Beforehand, a preliminary Finite Element Analysis was carried out in order to optimize the sensitivity of the technique to the micrometric defects. Our results indicate that the technique is proved to be quite successful in detecting flaws, with the added plus of being suitable for integration in the additive manufacturing equipment, thus allowing a continuous in-line inspection
| Reference Key |
montinaro2018fratturaa
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;N. Montinaro;D. Cerniglia;G. Pitarresi |
| Journal | applied catalysis |
| Year | 2018 |
| DOI |
10.3221/IGF-ESIS.43.18
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.