sharp contact corners, fretting and cracks
Clicks: 179
ID: 218394
2013
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
179 views
29 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #24 of 46 articles by views in applied catalysis
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Contacts with sharp edges subject to oscillatory loading are likely to nucleate cracks from the corners, if the loading is sufficiently severe. To a first approximation, the corners behave like notches, where the local elastic behaviour is relieved by plasticity, and which in turn causes irreversibilities that give rise to crack nucleation, but also by frictional slip. One question we aim to answer here is; when is the frictional slip enveloped by plastic slip, so that the corner is effectively a notch in a monolithic material? We do this by employing the classical Williams asymptotic solution to model the contact corner, and, in doing so, we render the solution completely general in the sense that it is independent of the overall geometry of the components. We then re-define the independent parameters describing the properties of the Williams solution by using the inherent length scale, a procedure that was described at the first IJFatigue and FFEMS joint workshop [1]. By proceeding in this way, we can provide a self-contained solution that can be ‘pasted in’ to any complete contact problem, and hence the likelihood of crack nucleation, and the circumstances under which it might occur, can be classified. Further, this reformulation of Williams' solution provides a clear means of obtaining the strength (defined by crack nucleation conditions) of a material pair with a particular contact angle. This means that the results from a test carried out using a laboratory specimen may easily be carried over to any complicated contact problem found in engineering practice, and a mechanical test of the prototypical geometry, which may often be quite difficult, is avoided.
| Reference Key |
hills2013fratturasharp
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;D. A. Hills;R. C. Flicek;D. Dini |
| Journal | applied catalysis |
| Year | 2013 |
| DOI |
10.3221/IGF-ESIS.25.05
|
| URL | |
| Keywords | Keywords not found |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.