enhanced hydrogen generation properties of mgh2-based hydrides by breaking the magnesium hydroxide passivation layer
Clicks: 226
ID: 215372
2015
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
226 views
34 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #218 of 526 articles by views in acs combinatorial science
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 526 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Due to its relatively low cost, high hydrogen yield, and environmentally friendly hydrolysis byproducts, magnesium hydride (MgH2) appears to be an attractive candidate for hydrogen generation. However, the hydrolysis reaction of MgH2 is rapidly inhibited by the formation of a magnesium hydroxide passivation layer. To improve the hydrolysis properties of MgH2-based hydrides we investigated three different approaches: ball milling, synthesis of MgH2-based composites, and tuning of the solution composition. We demonstrate that the formation of a composite system, such as the MgH2/LaH3 composite, through ball milling and in situ synthesis, can improve the hydrolysis properties of MgH2 in pure water. Furthermore, the addition of Ni to the MgH2/LaH3 composite resulted in the synthesis of LaH3/MgH2/Ni composites. The LaH3/MgH2/Ni composites exhibited a higher hydrolysis rate—120 mL/(g·min) of H2 in the first 5 min—than the MgH2/LaH3 composite— 95 mL/(g·min)—without the formation of the magnesium hydroxide passivation layer. Moreover, the yield rate was controlled by manipulation of the particle size via ball milling. The hydrolysis of MgH2 was also improved by optimizing the solution. The MgH2 produced 1711.2 mL/g of H2 in 10 min at 298 K in the 27.1% ammonium chloride solution, and the hydrolytic conversion rate reached the value of 99.5%.
| Reference Key |
ouyang2015energiesenhanced
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Liuzhang Ouyang;Miaolian Ma;Minghong Huang;Ruoming Duan;Hui Wang;Lixian Sun;Min Zhu |
| Journal | acs combinatorial science |
| Year | 2015 |
| DOI |
10.3390/en8054237
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.