examination of calcium silicate cements with low-viscosity methyl cellulose or hydroxypropyl cellulose additive

Clicks: 134
ID: 214628
2016
Free PDF
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #950 of 1,324 articles by views in spectrochimica acta - part a: molecular and biomolecular spectroscopy

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 1,324 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
The purpose of this study was to improve the operability of calcium silicate cements (CSCs) such as mineral trioxide aggregate (MTA) cement. The flow, working time, and setting time of CSCs with different compositions containing low-viscosity methyl cellulose (MC) or hydroxypropyl cellulose (HPC) additive were examined according to ISO 6876-2012; calcium ion release analysis was also conducted. MTA and low-heat Portland cement (LPC) including 20% fine particle zirconium oxide (ZO group), LPC including zirconium oxide and 2 wt% low-viscosity MC (MC group), and HPC (HPC group) were tested. MC and HPC groups exhibited significantly higher flow values and setting times than other groups (p<0.05). Additionally, flow values of these groups were higher than the ISO 6876-2012 reference values; furthermore, working times were over 10 min. Calcium ion release was retarded with ZO, MC, and HPC groups compared with MTA. The concentration of calcium ions was decreased by the addition of the MC or HPC group compared with the ZO group. When low-viscosity MC or HPC was added, the composition of CSCs changed, thus fulfilling the requirements for use as root canal sealer. Calcium ion release by CSCs was affected by changing the CSC composition via the addition of MC or HPC.
Reference Key
baba2016biomedexamination Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors ;Toshiaki Baba;Yasuhisa Tsujimoto
Journal spectrochimica acta - part a: molecular and biomolecular spectroscopy
Year 2016
DOI
10.1155/2016/4583854
URL
http://dx.doi.org/10.1155/2016/4583854
Keywords
Medicine

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.