electroless deposition of ni-p/sio2 composite coating
Clicks: 134
ID: 201760
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
134 views
27 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #325 of 391 articles by views in Talanta
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 391 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Electroless deposit Ni–P/SiO2 composite coating was performed on the steel substrate, DIN EN 10130. The preparation of nickel coating included two main steps. In the first step, the fraction of SiO2 particles sized the tens of nanometres was obtained by sedimentation. In the second step, the composite coating was plated on the steel substrate. The actual deposition process contains the deposition of plain Ni-P interlayer which served as the nucleation center for the deposition of Ni-P/SiO2 composite coating with co-deposited SiO2 particles. The morphology of deposited composite coating was studied by scanning electron microscope (SEM). Amount of individual elements in deposited coatings was determinated by EDS analysis. The microhardness of deposited composite coating was subsequently compared with microhardness value of the plain Ni–P coating.
| Reference Key |
buchtk2016actaelectroless
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Martin Buchtík;Petr Kosár;Jaromír Wasserbauer;Martin Zmrzlý |
| Journal | Talanta |
| Year | 2016 |
| DOI |
10.11118/actaun201664051459
|
| URL | |
| Keywords | Keywords not found |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.