Preparation and performance of a BTDA-modified polyurea microcapsule for encapsulating avermectin.

Clicks: 276
ID: 19887
2019
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #28 of 60 articles by views in colloids and surfaces b, biointerfaces

Most read Least read

Bar heights use a square-root scale.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
A pesticide microcapsule was prepared by encapsulating avermectin (AVM) in a polyurea microcapsule via interfacial polymerization in acetic ether/water emulsion. The polyurea microcapsule was consisted of chitosan oligomer (CO) as the membrane material and diphenyl methane-4,4'-diisocyanate (MDI) as the crosslinker. A chemical modification was carried out by grafting a UV-absorbent, 3,3',4,4'-benzophenonetetracarboxylic dianhydride (BTDA), to CO before interfacial polymerization to enhance the UV-resistance of the microcapsule. The BTDA grafted CO (CO-BTDA) and the AVM microcapsules were characterized by a variety of instrumental techniques, including NMR, FTIR, UV-vis, GPC-LS, DLS, SEM and TEM. The in vitro release test showed that the polyurea microcapsule maintained the sustained release of AVM for a longer period (up to 120 h) in comparison with the commercial AVM formulations (within 24 h). The photodegradation test revealed that the polyurea microcapsule significantly reduced the AVM degradation and extended the half-life of AVM from 4.16 h to 9.43 h. The AVM degradation was further reduced by using the BTDA-modified polyurea microcapsule. The corresponding half-life was extended up to 17.33 h and can be mediated by changing the mass ratio of BTDA: CO during the synthesis of CO-BTDA. The use of polyurea microcapsule did not raise a concern about pesticide residue as no AVM was detected after the photodegradation test. In addition, the polyurea microcapsule itself was subject to degradation under sunlight exposure, which reduced its residue in the environment.
Reference Key
fu2019preparationcolloids Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Fu, Yabo;He, Haowei;Liu, Ran;Zhu, Lei;Xia, Yining;Qiu, Jing;
Journal colloids and surfaces b, biointerfaces
Year 2019
DOI
S0927-7765(19)30544-2
URL
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.