effect of power cycling and heat aging on reliability and imc growth of sn-5sb and sn-10sb solder joints
Clicks: 98
ID: 196869
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
29.1
/100
98 views
14 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #207 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Power cycle reliability of solder joints with Sn-5Sb (mass%) and Sn-10Sb (mass%) alloys was investigated. The effects of power cycling and heat aging on the growth of intermetallic compound (IMC) layers at the interfaces between Sn-Sb alloys and Cu plates were also investigated. In the power cycling test, the solder joint with Sn-10Sb has high reliability compared with that of Sn-5Sb. IMC layers grew in both joints with increasing number of power cycles. Compared with Sn-5Sb and Sn-10Sb, difference in growth kinetics of IMC layers was negligible. A similar tendency was observed in the heat aging test. Compared with the power cycling and the heat aging, growth of IMC layers at the aging temperature of 200°C is faster than that in the power cycling test at the temperature range of 100°C to 200°C, while that at the aging temperature of 100°C, the growth is slower. On the basis of the comparison between the power cycling and the heat aging, it was clarified that growth kinetics of IMC layers in the power cycling can be predicted by investigating growth kinetics of the IMC layer at the temperatures in the vicinity of the peak temperature in power cycling.
| Reference Key |
kobayashi2018advanceseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Tatsuya Kobayashi;Ikuo Shohji;Yusuke Nakata |
| Journal | bulletin of the korean chemical society |
| Year | 2018 |
| DOI |
10.1155/2018/4829508
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.